RTP EMI 2861-60A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y4mQIP_RTP-EMI-2861-60A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 2.0 | % | ASTM D955 |
| Moisture Content | 0.030 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1.38 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 1.38 | MPa | ASTM D412 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D412 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | < 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 182 - 210 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps. |
| Note Message | |
|---|---|
| 1 . | ESD STM11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultron® 150C4 | Asia International Enterprise (Hong Kong) Limited | PEI | Ultron® |
| ADDINYL B2 ZV50 | ADDIPLAST | Nylon 6 | ADDINYL |
| 3M™ Dyneon™ Fluoroelastomer MIP 8740 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Electroblend® ABS-1800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Electroblend® |
| LNP™ THERMOCOMP™ RC008H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |