LNP™ LUBRICOMP™ Lexan_LF1530A compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y4cHaD_LNPLUBRICOMPLexanLF1530Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP LEXAN_FL1530 compound is a 30% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.050 - 0.25 | % | Internal method |
| Transverse flow : 3.20mm | 0.15 - 0.35 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 114 | MPa | ASTM D638 |
| Fracture | 114 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 8410 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 560 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 18.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 129 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 266 - 288 | °C | |
| Middle Temperature | 277 - 299 | °C | |
| Front Temperature | 288 - 310 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 288 - 310 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-550S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| Stat-Tech™ AS-20CF/000 BK001 | PolyOne Corporation | ABS | Stat-Tech™ |
| Flexoprene® 85 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| PERLER® O07H3000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| Monprene® RG-12160 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |