| AX series resins are opaque polymer alloys with a high deflection temperature under load without reinforcement and a chemical resistance as high as those of crystalline resins. They are excellent in moldability and provide molded products fewer in the number of sink marks, warps, and runoffs. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.17 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 1.0 | -- | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.75 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 72.0 | 53.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | 70 | % | ASTM D638 |
| Flexural Modulus | 2600 | 1200 | MPa | ASTM D790 |
| Flexural Strength | 103 | 76.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 78 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | -- | °C | ASTM D648 |
| CLTE - Flow | 7.7E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | -- | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | -- | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | -- | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | -- | 0.040 | ASTM D150 | |
| Arc Resistance | -- | 84.0 | sec | ASTM D495 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Additional Information |
|---|
| 调节后的 Comp Track Index, IEC 60112: >600 V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203.3D | RTP Company | Nylon 612 | RTP |
| Bayblend® M850 XF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| LNP™ THERMOCOMP™ RFZ349XC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Plasmer 1080B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| LEXAN™ LUX9612G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |