Ultramid® A3WG3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y3SMhV_Ultramid-A3WG3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre reinforced and heat aging resistance injection moulding grade for machine components and housings of medium stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 60.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.7 to 7.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 to 2.5 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 145 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.61 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 240 | -- | °C | |
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 145 | -- | °C | |
| -- 3 | 175 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Pass | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | < 300 | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6000 | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 10 | % | ISO 527-2 |
| Tensile Creep Modulus 4(1000 hr) | -- | 2600 | MPa | ISO 899-1 |
| Flexural Modulus | 5500 | 4000 | MPa | ISO 178 |
| Flexural Stress | 200 | 125 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | |
| 23°C | 8.0 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 43 | -- | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 5.5 | 6.5 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 3.0E-5 to 3.5E-5 | 3.0E-5 to 3.5E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.0E-5 to 8.0E-5 | 7.0E-5 to 8.0E-5 | cm/cm/°C | |
| Specific Heat | 1800 | -- | J/kg/°C | |
| Thermal Conductivity | 0.33 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.30 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 80°C |
| 2 . | 20000 h |
| 3 . | 5000 h |
| 4 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HNR101 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Yanshan PE 6100M | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Clyrell RC5003 | PolyMirae | PP Random Copolymer | Clyrell |
| Colorite CS Series CS7559LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Exceed™ 4518 Series | ExxonMobil Chemical | mPE | Exceed™ |