Order Products : sales@su-jiao.com
BESTPOLUX PCBM/01
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | y38MND_BESTPOLUX-PCBM-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/PBT Blend natural lubricated and Impact modified |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 77 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 60 | kJ/m² | ISO 179 |
| 23°C | 80 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Humidity Pellets, ISO 1110: 0.2%Flammability Speed, FMV 302:<100 mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 245 - 255 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200.5 LF | RTP Company | PEEK | RTP |
| Qenos PE GM7655 White 22 | Qenos Pty Ltd | HDPE, HMW | Qenos PE |
| SCHULAMID® 66 MV HI | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sinvicomp SRP3003FRF | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Karina GRAY PVC COMPOUND 812-18/52-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |