Pyramid™ PPS SE2000
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xzTlHu_Pyramid-PPS-SE2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Pyramid™ PPS SE2000 is a Polyphenylene Sulfide (PPS) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 90.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4200 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 90.0 | °C | DSC |
| Melting Temperature | 280 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dissipation Factor (1 Hz) | 1.1E-3 | ASTM D150 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® VERSADUR® PP-C 570 Natural | SIMONA AMERICA, Inc. | PP Copolymer | SIMONA® VERSADUR® |
| Clariant Nylon 6/6 PA-111M40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Grilon® TSG-15/4 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Lupol® HI5204H | LG Chem Ltd. | TPO | Lupol® |
| POLYCOMPO PP J707G | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |