Grilamid® 2D 25 W 20 X nat
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xyaRz5_Grilamid-2D-25-W-20-X-nat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® 2D 25 W 20 X nat is a Polyamide 612 (Nylon 612) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or profile extrusion. Important attributes of Grilamid® 2D 25 W 20 X nat are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 39.0 | 30.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 600 | 400 | MPa | ISO 527-2 |
| Tensile Stress (50% Strain) | 30.0 | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | 13 | kJ/m² | |
| 23°C | No Break | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 115 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 210 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+10 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | 37 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA612-HIP, E, 22-005 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Comco PA 6 G high impact | Comco-Plastic GmbH | Nylon 6 | Comco |
| Karina CLEAR PVC COMPOUND 80/224-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST EP 1500GY166 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| 3M™ Dyneon™ Fluoroplastic FEP FLEX6305Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Starex NH-0825 S | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |