Badamid® LA70 K MoS21%
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xxnFvo_Badamid-LA70-K-MoS21-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing injection moulding grade for short cycle times, lubricated with MoS2, high wear resistance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.0 to 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 to 3.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 3700 | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress 2 | ISO 527-2/50 | |||
| Yield, 23°C | -- | 60.0 | MPa | |
| Break, 23°C | 95.0 | 45.0 | MPa | |
| Tensile Strain 3 | ||||
| Yield, 23°C | -- | 17 | % | ISO 527-2/50 |
| Break, 23°C | 4.0 | 80 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 130 kJ/m² | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/B |
| Melting Temperature (DSC) 4 | 260 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 5 | 118 | -- | °C | |
| -- | > 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.20 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/min |
| 5 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HiFill® TPX-HTN-01026 A | Techmer Engineered Solutions | Nylon, Unspecified | HiFill® |
| Huafon EP127 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| SECCO LL0209AA | Shanghai SECCO Petrochemical Co., Ltd | LLDPE | SECCO |
| Tunhe PBT TH6075 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |
| Sylvin 9703-66 Red 6274 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |