AZDEL™ R451-B01
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | AZDEL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xxbG76_AZDEL-R451-B01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL R451-B01 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat contained within polypropylene resin matrix. This composite material features high flow properties and a generally homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6920 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 7050 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 4.00 mm, Energy at Peak Load | 16.3 | J | ASTM D3763 |
| 4.00 mm, Total Energy | 31.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 159 | °C | ASTM D648 |
| CLTE - Flow (-40 to 121°C) | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Basis Weight, Internal Test Method: 0.93 lbs/ft²Filler Content by Weight(ashing), Internal Test Method: 45 %Multi-axial Impact Peak Force, ASTM D3763, 4mm: 940 lbsNotched Izod Impact, ISO 180, 23°C, 4mm: 1025 J/mPoissons Ratio, ISO 527: 0.37Sheet Thickness, Internal Test Method: 145 milsSpecific Gravity, ASTM D792, Laminated: 1.23Specific Gravity, ASTM D792, Molded: 1.27 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3850H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Exxtral™ Performance Polyolefin LNV010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| DURACON® M25LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Huafon JF-P-6881 / JF-I-6820 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7301BZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |