Starpylen HW 30K ECR
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xwYatq_StarpylenHW30KECR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen HW 30K ECR-BK is a reinforced Polypropylene with a low carbon footprint spherical filler, Injection Molding Resin (also known as HW30KECR). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.70 | cm³/10min | ISO 1133 |
| shrinkage- Flow (4.00 mm) | 2.2 - 2.4 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed, 64.0 mm Span) | 56.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 - 205 | °C | |
| Middle Temperature | 215 - 225 | °C | |
| Front Temperature | 225 - 250 | °C | |
| Processing (Melt) Temp | 225 - 250 | °C | |
| Mold Temperature | 30 - 50 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Vydyne® R525H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Innothane® IE-60DC | Innovative Polymers, Inc. | TSU | Innothane® |
| Leona™ FG173 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ LUBRICOMP™ UX05051 compound | SABIC Innovative Plastics Europe | PPA | LNP™ LUBRICOMP™ |