POLYfill PP CIP6015F
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xvumEk_POLYfill-PP-CIP6015F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 to 1.1 | % | |
| Flow | 0.90 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 24.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 55 | % | |
| Flexural Modulus (23°C) | 1800 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Scratch Resistance - 10 N Fine Structure | 0.120 | dL | ISO 1518/D65 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ISO 306/A50 |
| -- | 63.0 | °C | ISO 306/B50 |
| CLTE - Flow | 6.0E-5 to 8.0E-5 | cm/cm/°C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENYL 66 3040 MQ | Vamp Tech | Nylon 66 | DENYL |
| DI-COAT E-4599 | Hapco Inc. | TP, Unspecified | DI-COAT |
| Fluoroplex R 25 - GMA | UNIFLON | PTFE | Fluoroplex |
| ELASTOSIL® LR 3844/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Iupilon® MB9000 | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |