Kingfa PBT T15
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xtS4n2_Kingfa-PBT-T15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT T15 is a polybutene terephthalate (PBT) material, which contains 15% mineral fillers. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT T15 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.90 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 3 | 2800 | MPa | ASTM D790 |
| Flexural Strength 4 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 195 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 280°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RGN120 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| RJM SL701M4VV | RJM International, Inc. | PP, Unspecified | RJM |
| Network Polymers PP 30 0500 GF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| KOPLA PA66 KDG1030 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| ICORENE® N6501 | ICO Polymers EMEA, A Division of A. Schulman | PS (HIPS) | ICORENE® |