Hyundai EP PA6 LS140
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xtIE6a_Hyundai-EP-PA6-LS140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP PA6 LS140 is a Polyamide 6 (Nylon 6) product filled with 20% glass fiber. It is available in Asia Pacific. Primary characteristic: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Ash Content | 20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 118 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5490 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 202 | °C | ASTM D648 |
| Melting Temperature | 220 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 3.8 | kV/mm | ASTM D149 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2300 A AR 15 TFE 15 | RTP Company | TPU-Polyester | RTP |
| ARMAMID® PA NE 30-1ETM | Poly Plastic | Nylon 6 | ARMAMID® |
| Elvaloy® AC 3717 | DuPont Packaging & Industrial Polymers | EnBA | Elvaloy® |
| KPOL-NYLON K-NY66/21I | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| SCHULAKETON CF 20 | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |