CELEX™ 350
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xrGbpe_CELEX-350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CELEX 350 is a 50% glass fiber reinforced polycarbonate resin. It is designed with high rigidity and good dimensional stability for use in structural parts of printer, scanner and copier. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 121 | MPa | ASTM D638 |
| Flexural Modulus | 10100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® HT GF 30 | A. Schulman Europe | PCT | SCHULADUR® |
| Vi-Chem PVC VNC 110I-7261 | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| Yanshan PE LD188 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| APEX® 3202-65NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Formolene® 3435E | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |