| Nanocomposite based on a ABS/PA-Blend for high dimensional stability |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 4.00 | -- | cm³/10min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 85.0 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1250 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 39.0 | 28.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.0 | 14 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 30 | 110 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 97.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 77.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 194 | -- | °C | ISO 306/A50 |
| -- | 116 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 27 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.5 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.5 mm | 650 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.5 mm | 675 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 675 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M20TCPP12 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| VESTOLIT® B 7521 Ultra | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| Toyolac® 100 MPM | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Halene H R5801 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| Kepamid® 2313GFS | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |