| Category: | PC , Polycarbonate |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xplGfW_Integra-PC-5027-F1.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| High Viscosity, UV Stabilized Polycarbonate |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 70.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2250 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 91.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 910 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 135 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6926 NA 022 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| KPOL-LLDPE LL K-1.1/918 | KPOL Chem Co. | LLDPE | KPOL-LLDPE |
| Karina BLACK PVC COMPOUND -E TR-550-DA-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP CPP-310 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| POFEX EP8300S 95A/95C | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |