LNP™ THERMOCOMP™ JF004 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xpgUGV_LNPTHERMOCOMPJF004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound JF-1004 Product reorder name: JF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.74 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7360 | MPa | ASTM D638 |
| -- | 7590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 114 | MPa | ASTM D638 |
| Fracture | 109 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.8 | % | ASTM D638 |
| Fracture | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6690 | MPa | ASTM D790 |
| -- | 6420 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 186 | MPa | ASTM D790 |
| -- | 183 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| 23°C 3 | 73 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.8 | J | ASTM D3763 |
| -- | 4.49 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 206 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 205 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2204 LF | RTP Company | PEEK | RTP |
| Ultramid® Endure D3G10 BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| BJB Silicone TC-5024 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| Alpha PVC GW 2403-1-VW1 NATURAL 105-LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Axiall PVC 17900 | Axiall Corporation | PVC, Flexible | Axiall PVC |