LNP™ THERMOCOMP™ LC006 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xpT0nX_LNP-THERMOCOMP-LC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* LC006 is a compound based on Polyetheretherketone resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound LC-1006 Product reorder name: LC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.12 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 30800 | MPa | ASTM D638 |
| -- | 24700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 226 | MPa | ASTM D638 |
| Break | 230 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 20200 | MPa | ASTM D790 |
| -- | 24300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 325 | MPa | ASTM D790 |
| -- | 347 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.30 | ||
| vs. Itself - Static | 0.32 | ||
| Wear Factor - Washer | 55.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 7.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 610 | J/m | ASTM D4812 |
| 23°C 3 | 43 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 12.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | > 299 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | > 299 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | > 240 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.9E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.770 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PC 1005 GF 10 FL UV | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| Cellophane™ 400PC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Epoxies, Ect. 20-3004 HV | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| RONFALIN® SAN 4501 GF35 | A. Schulman Europe | SAN | RONFALIN® |
| Sylvin 9600-55 Clear Blue 8259 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |