SD POLYCA™ 875G10
| Category: | PC , Polycarbonate |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xpOXIt_SDPOLYCA875G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SD POLYCA™ 870 series, SI8001H and SI6001W are based on silicone type flame retardants instead of conventional bromine type and phosphonate type flame retardants. SD POLYCA 870 series, SI8001H and SI6001W are environmentally friendly polycarbonate resins and show excellent hydrolysis resistance, thermal stability, heat resistance and molding capability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 73.0 | MPa | ASTM D638 |
| -- | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 4.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3630 | MPa | ASTM D790 |
| -- | 3600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 111 | MPa | ASTM D790 |
| -- | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2201H1W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TABOREN PC 52 T 20 | SILON s.ro | PP Copolymer | TABOREN |
| TAROPRENE® 1 A60 M1M | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Dartek B-850 | DuPont Canada, Inc. - Dartek Division | Nylon 66 | Dartek |
| DENKA EVA TEX NA500 | Denka Company Limited | EVA | DENKA EVA TEX |