Tuftec™ H1121
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Tuftec™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xpCv70_Tuftec-H1121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Specially designed as a modifier and compatibilizer for polypropylene (PP). Ultrafine dispersion in PP, due to outstanding compatibility, enabling production of transparent sheets and films with excellent flexibility and resistance to hazing or whitening under bending or folding. It is supplied in pellet form. Excellent substitute for PVC, due to unique combination of transparency and flexibility of PP/H1221 blends. Transparent apparel packaging and carrying cases. Folders and toys, enabled by flexibility and absence of hazing and whitening at folds and bends. Soft, comfortable surface feel, enabling excellent elastic films for bag liners, tarpaulins, signboards, other products. Compatibilizer. Basepolymer for SEBS molding compounds. Adhesives and sealants component. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, Injection Molded | 23.0 | MPa | |
| Break, Injection Molded | 28.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 530 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 710 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3/2 | ||
| MD : 70 µm | 340 | MPa | |
| TD : 70 µm | 380 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 5.00 | MPa | |
| TD : Yield | 5.00 | MPa | |
| MD : Break | 13.0 | MPa | |
| TD : Break | 13.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 70 | % | |
| TD : Break | 71 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -21.4 | °C | ASTM D746 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (70.0 µm) | 92.4 | % | ASTM D1003 |
| Haze (70.0 µm) | 4.2 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Whitening | 3.2 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sanren M3700C (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Torelina® A673M | Toray Resin Company | PPS | Torelina® |
| Vydyne® R540H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| NORYL GTX™ GTX951W resin | SABIC Innovative Plastics Asia Pacific | PPE+PS+Nylon | NORYL GTX™ |