EMAC® SP2255
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | EMAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xp67R2_EMAC-SP2255.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their use as bases for all-purpose concentrates for addition to a wide spectrum of polymers. They process like LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Methyl Acrylate Content | 17.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 37 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 12.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 730 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 52.0 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 62.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 470 | % | |
| TD : Break, 38 µm, Blown Film | 720 | % | |
| Dart Drop Impact (38 µm, Blown Film) | 300 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 70 | g | |
| TD : 38 µm, Blown Film | 400 | g | |
| Seal Initiation Temperature | 68.0 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -73.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 60.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 82.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm, Blown Film) | 15 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 53 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-88S | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| PRL PC-HM-FR1 | Polymer Resources Ltd. | PC | PRL |
| KOCETAL® UR304 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Sylvin 83045-67 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4225-75 White 1498 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |