KIBILAC® PW-957
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBILAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xoXH5s_KIBILAC-PW-957.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KIBILAC® PW-957 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 26.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break | 38.0 | MPa | ISO 527-2/50 |
| 3.18 mm 1 | 43.1 | MPa | ASTM D638 |
| Tensile Strain (Break) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 3 | 63.7 | MPa | ASTM D790 |
| -- 4 | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 150 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| -- | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm 5 | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 6.35 mm 6 | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525, ISO 306/A50 7 7 |
| -- | 107 | °C | ISO 306/A120 |
| -- | 92.0 | °C | ISO 306/B50 |
| -- | 95.0 | °C | ISO 306/B120 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 97 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 240 | °C | |
| Front Temperature | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 120°C/hr |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ 403/450 NAT | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| SILVER® SA-5323 | Guangdong Silver Age Sci & Tech. Co., Ltd | Polyolefin, Unspecified | SILVER® |
| TOTAL Polyethylene XSene® HDPE XS 10B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| AFFINITY™ GA 1900 | The Dow Chemical Company | POP | AFFINITY™ |
| AFLAS® 150L | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |