| Polymamide 6 Compound resin, High viscosity, wide uses |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 1.8 | % | ASTM D570 |
| Color b (23°C) | -4.00 - -1.00 | ||
| Color L (23°C) | 70.0 - 75.0 | ||
| Moisture Content (23°C) | % | Karl Fisher | |
| Relative viscosity- 96% H2S04 (23°C) | 3.47 - 3.57 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Chip Size (23°C) | 135 - 155 | ea/g | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 74.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 65 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2680 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 180 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2282 HF TFE 15 | RTP Company | PEEK | RTP |
| AEI SX703:CM488-6 | AEI Compounds Limited | HDPE | AEI |
| Andur 8-5 APLF/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| Formolene® 4181T | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Axiall PVC 4100-50 | Axiall Corporation | PVC, Flexible | Axiall PVC |