Versaflex™ OM 1060X-1
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xoLmSL_Versaflex-OM-1060X-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Versaflex™OM 1060X-1 is a TPE designed to bond PC or ABS matrix materials in an overlapping molding manner.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 17 - 27 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 26 - 36 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 - 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 23°C 2 | 2.14 | MPa | ASTM D412 |
| 300% strain, 23°C 3 | 3.24 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 4.10 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 490 | % | ASTM D412 |
| Tear Strength | 26.3 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 29 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 11200 sec^-1) | 12.2 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 166 - 188 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 193 - 227 | °C | |
| Nozzle Temperature | 210 - 238 | °C | |
| Processing (Melt) Temp | 193 - 221 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Back Pressure | 0.00 - 0.862 | MPa | |
| Screw Speed | 75 - 125 | rpm |
| Injection instructions |
|---|
| 以乙烯醋酸乙烯共聚物 (EVA) 或低密度聚乙烯 (LDPE) 为基础的色母料最适合 Versaflex™ OM 1060X-1 着色。典型的母料浓度为 50:1 到 25:1 - 要最大限度减少对粘接的影响，用量应该尽可能低。若使用 GLS 可供的预着色复合材料，则可达到较好的配色一致性。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versaflex™ OM 1060X-1 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versaflex™ OM 1060X-1 具有良好的熔体稳定性。最长停留时间可能会根据机筒尺寸有所变化。通常，如果机器闲置 5 - 8 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 3 英寸/秒第一阶段 - 提升压力：300 - 900 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：3 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | Mouth die c |
| 3 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF 25 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| TRIREX® Compound HF3000HG10 | Samyang Corporation | PC | TRIREX® Compound |
| GLS PP ZT89 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Hostacom PPR 1042 101070 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Deprene 251-80 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |