CYCOLOY™ XCY620S resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xoHNap_CYCOLOY-XCY620S-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ ABS Automotive applications |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/5.0 kg | 20.0 | cm³/10min | |
| 265°C/5.0 kg | 25.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.13 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 54.0 | MPa | |
| Break | 56.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.5 | % | |
| Break | 100 | % | |
| Flexural Modulus | |||
| 50.0 mm Span 1 | 2300 | MPa | ASTM D790 |
| -- 2 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 82.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 3 | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | ||
| -30°C | 45 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength 5(23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 6 | ISO 180/1A | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 65.0 | J | |
| 23°C, Total Energy | 55.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 106 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 129 | °C | ASTM D1525 9 |
| -- | 130 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | ||
| 100°C 10 | Pass | ||
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 39 | kV/mm | |
| 1.60 mm, in Oil | 25 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 240 to 280 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*3 sp=62mm |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| 9 . | Rate B (120°C/h), Loading 2 (50 N) |
| 10 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vistalon™ 703 | ExxonMobil Chemical | EPM | Vistalon™ |
| VALOX™ ENH3500 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| APEX® 74-8208-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Cevian®-V 300, 300SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| InnoPlus HD3001C | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |