TOTAL Polyethylene Lumicene® M 2710 EP (EU) Datasheet,LLDPE,TOTAL Refining & Chemicals-SHANGHAI SUSHENG

Message
Lumicene® mPE M 2710 EP is a second generation metallocene based Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 2710 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 2710 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 2710 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, collation shrink and lamination.

General Information
Additive	Processing Aid
Features	Good Heat Seal Good Stiffness Good Tear Strength Heat Sealable Hexene Comonomer High Clarity High Gloss Puncture Resistant
Uses	Bags Blending Consumer Applications Film Food Packaging Industrial Applications Laminates Multilayer Film Packaging Shrink Wrap
Agency Ratings	EC 1907/2006 (REACH)
Forms	Pellets
Processing Method	Coextrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.927	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)
190°C/2.16 kg	0.90	g/10 min	ASTM D1238, ISO 1133
190°C/21.6 kg	30	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (vs. Itself - Static, Blown Film)	0.50		ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus			ASTM D882A
1% Secant, MD : 25 µm, Blown Film	214	MPa
1% Secant, TD : 25 µm, Blown Film	172	MPa
Tensile Stress
MD : Yield, 40 µm, Blown Film	13.5	MPa	ISO 527-3
TD : Yield, 40 µm, Blown Film	14.0	MPa	ISO 527-3
MD : Break, 25 µm, Blown Film	33.8	MPa	ASTM D882A
TD : Break, 25 µm, Blown Film	33.1	MPa	ASTM D882A
MD : Break, 40 µm, Blown Film	51.0	MPa	ISO 527-3
TD : Break, 40 µm, Blown Film	48.0	MPa	ISO 527-3
Tensile Elongation
MD : Break, 25 µm, Blown Film	580	%	ASTM D882A
TD : Break, 25 µm, Blown Film	720	%	ASTM D882A
MD : Break, 40 µm, Blown Film	650	%	ISO 527-3
TD : Break, 40 µm, Blown Film	720	%	ISO 527-3
Dart Drop Impact
25 µm, Blown Film	150	g	ASTM D1709A
40 µm, Blown Film	200	g	ISO 7765-1
Elmendorf Tear Strength - TD (25 µm, Blown Film)	500	g	ASTM D1922
Seal Initiation Temperature (25 µm, Blown Film)	112	°C
Water Vapor Transmission	14	g/m²/24 hr	ASTM E96
Elmendorf Tear Strength ¹			ISO 6383-2
MD : 40.0 µm	60.0	kN/m
TD : 40.0 µm	160.0	kN/m

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	118	°C	ISO 306
Melting Temperature
--	119	°C	ISO 11357-3
--	121	°C	ASTM D3417

Optical	Nominal Value	Unit	Test Method
Gardner Gloss (45°, 25.4 µm, Blown Film)	65		ASTM D523
Gloss (45°, 40.0 µm, Blown Film)	70		ASTM D2457
Haze
25.4 µm, Blown Film	7.0	%	ASTM D1003
40.0 µm, Blown Film	6.5	%	ISO 14782

Extrusion	Nominal Value	Unit
Melt Temperature	193 to 210	°C

Note Message
1 .	Blown Film

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xo86aL_TOTAL-Polyethylene-Lumicene-M-2710-EP-EU-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Medalist® MD-50138D	Teknor Apex Company	TPE	Medalist®
Ultradur® B 4441 G5	BASF Corporation	PBT	Ultradur®
Niblend F17	Soredi S.p.a.	PC+ABS	Niblend
Bapolan® PS6130	Bamberger Polymers, Inc.	PS (GPPS)	Bapolan®
IROCOAT® CA-271	Huntsman Corporation	TPU, Unspecified	IROCOAT®