IROGRAN® A 87 P 4946
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xnq0G8_IROGRAN-A-87-P-4946.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 87 P 4946 is a polyether based thermoplastic polyurethane intended for injection moulding and extrusion applications. IROGRAN A 87 P 4946 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with high extrudability. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 65.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 87 | ||
| Shore D, Injection Molded | 38 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 35 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 8.27 | MPa | ASTM D412 |
| 100% Strain | 7.00 | MPa | DIN 53504 |
| 300% Strain | 12.4 | MPa | ASTM D412 |
| 300% Strain | 11.0 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 30.3 | MPa | ASTM D412 |
| Break | 40.0 | MPa | DIN 53504 |
| Tensile Elongation 5(Break) | 650 | % | ASTM D412, DIN 53504 |
| Tear Strength 6 | |||
| -- | 98.1 | kN/m | ASTM D624 |
| -- | 60 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Hopper Temperature | 23.9 to 35.0 | °C | |
| Rear Temperature | 185 to 195 | °C | |
| Middle Temperature | 185 to 195 | °C | |
| Front Temperature | 185 to 195 | °C | |
| Nozzle Temperature | 185 to 200 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 175 to 185 | °C | |
| Cylinder Zone 2 Temp. | 175 to 185 | °C | |
| Cylinder Zone 3 Temp. | 175 to 185 | °C | |
| Cylinder Zone 4 Temp. | 175 to 185 | °C | |
| Cylinder Zone 5 Temp. | 175 to 185 | °C | |
| Adapter Temperature | 185 to 195 | °C | |
| Die Temperature | 185 to 195 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3940CH | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Vi-Chem PVC V221-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Wellamid® GF30-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Evermore PUR SS-168K | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| DJSilicone NE-Z260 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |