Kingfa JH710 G20
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xneR7T_Kingfa-JH710-G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa JH710 G20 is a polycarbonate alloy (PC alloy) material, which contains a 20% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa JH710 G20 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 96.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 6200 | MPa | ASTM D790 |
| Flexural Strength 4 | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 90 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 146 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 132 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 235 - 270 | °C | |
| Mold Temperature | 90.0 - 130 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 290°CInjection Speed: 60 to 80% |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® ET UV540 | Covestro - Polycarbonates | PC | Makrolon® |
| FLEXITEQ™ F65A110 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| DynaStat® 157-SA | Polymer Dynamix | TPO | DynaStat® |
| ICORENE® 9005 | ICO Polymers EMEA, A Division of A. Schulman | Nylon 12 | ICORENE® |
| LUVOCOM® 1106-8380/WT | LEHVOSS Group | PEI | LUVOCOM® |