Nycast SLX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Cast Nylons Ltd. |
| Trademark: | Nycast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xmOvyh_Nycast-SLX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SLX joins the Nycast® family of premium bearing grades as an engineering and design solution for bearing and wear applications. Nycast® SLX closes the gap between static and dynamic coefficients of friction with superior performance where customers require the best material for overcoming "stick-slip" tendencies. Unlike the competition, Cast Nylons Limited offers SLX in all our standard stock shape configurations. We never limit your design to only a few options. This is one more reason to put the Nycast® Advantage to work for you. Manufactured with a proprietary lubrication package, Nycast® SLX is available as plate up to 4" thick, rod up to 12" diameter, and tubular bar up to 40" diameter. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 to 1.14 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.032 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 to 120 | ASTM D785 | |
| Durometer Hardness (Shore D) | 75 to 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3170 | MPa | ASTM D638 |
| Tensile Strength | 69.6 to 70.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 38 to 47 | % | ASTM D638 |
| Flexural Modulus | 2510 to 2590 | MPa | ASTM D790 |
| Flexural Strength | 86.9 to 89.6 | MPa | ASTM D790 |
| Compressive Modulus | 1870 to 1970 | MPa | ASTM D695 |
| Compressive Strength | 101 to 112 | MPa | ASTM D695 |
| Shear Strength | 58.9 to 59.2 | MPa | ASTM D732 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.14 to 0.19 | ||
| vs. Itself - Static | 0.12 to 0.14 | ||
| Deformation Under Load | 0.510 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 74 to 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 70.0 to 72.2 | °C | |
| Melting Temperature | 221 | °C | |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Aceso® Lumicene® MR 10MM0 S01 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| NIMA NH OP66GF25 FR | Ovation Polymers Inc. | PESU | NIMA |
| Axiall PVC 8753 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elvakon® 4490 | Lucite International Inc. | Acrylic (PMMA) | Elvakon® |
| Karina NATURAL PVC COMPOUND -E 730D25/ 1-IS-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |