NORYL™ RN0611 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xlm3vh_NORYL-RN0611-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL RN0611 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0611 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/1.2 kg | 17.0 | cm³/10min | |
| 280°C/2.16 kg | 35.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break | 5.0 | % | ASTM D638 |
| Break | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 30 | J/m | ASTM D256 |
| 23°C | 38 | J/m | ASTM D256 |
| -30°C 9 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 93.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 94.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 77.0 | °C | ISO 75-2/Af |
| 1.8 MPa, Annealed, 3.20 mm | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 101 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.70 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 2.9E-3 | ASTM D150, IEC 60250 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 65.0 to 85.0 | °C | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 260 to 295 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 260 to 295 | °C | |
| Mold Temperature | 45.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® C3 HH GF60 | Nilit Plastics | Nylon 66/6 | NILAMID® |
| ALTECH® NXT PP-B A 2035/450 GF35 CP | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® NXT PP-B |
| Chansieh Phenolic J-661 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| AvaSpire® AV-630 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| MACOMASS PP MM-PP HI 22 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |