Jampilen RP230C
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xlk5WW_JampilenRP230C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Jampilen RP230C" is a natural polypropylene random copolymer for extrusion applications which contains an enhanced stabilization package. It is specially suitable for pipe and fttings having high impact resistance. Features:
Typical Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 12 | % | ASTM D638 |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 3 |
| Melting Temperature (DSC) | 148 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 C SI 2 | RTP Company | PPS | RTP |
| RTP 203D HS TFE 15 | RTP Company | Nylon 612 | RTP |
| SUMILITE® PL-1640 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Generic Cellulose, Regenerated | Generic | Cellulose, Regenerated | Generic |
| Dutral® TER 4039 | Versalis S.p.A. | EPDM | Dutral® |