VENELENE® 11O1
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xiaVgs_VENELENE-11O1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Film Puncture Force (35 µm) | 10.8 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 35 µm | 55.0 | MPa | ASTM D882 |
| TD : Fracture, 35 µm | 44.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 35 µm | 760 | % | ASTM D882 |
| TD : Fracture, 35 µm | 850 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 35 µm | 1000 | g | ASTM D1922 |
| TD : 35 µm | 1700 | g | ASTM D1922 |
| Impact Resistance, Film | 530 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 160 | MPa | ASTM D882 |
| TD | 145 | MPa | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (35.0 µm) | 85.0 | % | ASTM D1003 |
| Haze (35.0 µm) | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 210 | °C |
| Extrusion instructions |
|---|
| Inverted Extrusion profile (descendent). Blow up ratio (BUR): 2 - 3. Die gap: 0.9 a 1.5 mm. Frost line Height: 4 - 5 times Die Diameter. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 MI | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Conpol™ 10AF | DuPont Packaging & Industrial Polymers | EMAA | Conpol™ |
| HiFill® PP 0320 S1 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| INLUBE PA66GF30TF15IM | Infinity LTL Engineered Compounds | Nylon 66 | INLUBE |
| Karina IVORY PVC COMPOUND 900-35/ 1-AYR-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |