Victron® 095
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | Victron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xhlOrm_Victron-095.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketones (Abbr. PEEK) is a crystalline high performance polymer with outstanding heat resistance, excellent strength and thermal properties. PEEK can compete with metals in lots of fields, its uniquely structure and properties offer outstanding fatigue and abrasion resistances, self-lubricated, excellent electrical properties, radiation resistance, and can withstand extreme temperatures difference environments. PEEK are highly used in electronics and electrical, automotives, mechanical and chemical, aerospace, military, and many high-end industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.70 | % | |
| Water Absorption (Saturation, 23°C) | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 99 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 95.0 | MPa | ISO 527-2/1270 |
| Tensile Strain (Break) | > 70 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Flexural Stress 2 | 165 | MPa | ISO 178 |
| Abrasion (23°C) | 0.340 | ISO 8295 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | > 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 315 | °C | ISO 306/B50 |
| CLTE - Flow (-20 to 150°C) | 4.7E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.25 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (in Oil) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resblend ABS/PC | Polimarky Spolka Jawna | PC+ABS | Resblend |
| S-RIM™ 7240 Black | Hapco Inc. | TP, Unspecified | S-RIM™ |
| Sylvin 2812-80 White 1440 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Alcryn® 5080 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| BMC 700 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |