MALEX 01FN002 - 5251
| Category: | PC , Polycarbonate |
| Manufacturer: | AD majoris |
| Trademark: | MALEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xhQaOK_MALEX-01FN002---5251.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MALEX 01FN002 - 5251 is a low viscosity polycarbonate (PC) resin and contains a release agent to ensure easy processing, intended for injection moulding. The product is available in bordeaux (MALEX 01FN002 - 5251 ) but other colours can be provided on request They combine high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS MALEX 01FN002 - 5251 is intended for the injection moulding of electrical components and automotive applications including interior, and electrical and mechanical systems, such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C) | 0.35 | % | DIN 53495 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 133 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/B50 |
| -- | 141 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength (0.800 mm, in Oil) | 17 27 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 | ||
| Arc Resistance | 119 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.500 to 1.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV300 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Chemlon® 60GSF6 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| CP PRYME® Nylon 612 NST143G | Chase Plastics Services Inc. | Nylon 612 | CP PRYME® Nylon 612 |
| Evoprene™ G 927 | AlphaGary | SEBS | Evoprene™ G |
| Plexiglas® Diffuse V045-68194 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |