| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xghxLV_AEI-SX703-CM488-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Silane crosslinkable, high density polyethylene for injection moulding SX703 is a silane grafted HDPE compound curable by exposure to moist conditions. It is specifically designed for high output processing by conventional thermoplastic injection moulding. The graft component SX703 is mixed with a crosslinking catalyst masterbatch CM488-6 generally in the ratio 95:5. This material combines good flow, high rigidity and excellent notched impact strength. The two component system SX703:CM488-6 has high degree of crosslinking which gives it useful strength at temperatures not usually reached by HDPE. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | BS 2782 620A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | Internal method |
| Environmental Stress-Cracking Resistance | 20.0 | hr | ASTM D1693A |
| Gel Content | 65 | % | ASTM D2765 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | 160 | mm³ | ISO 4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | 50 | % | IEC 60811-2-1 |
| Permanent elongation after cooling | 0.0 | % | IEC 60811-2-1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Crosslinking - In hot water | |||
| 95 to 100°C, 1.00mm | 5.0 | hr | |
| 95 to 100°C, 2.00mm | 12.0 | hr | |
| 95 to 100°C, 3.00mm | 24.0 | hr |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant | 900 | MPa | BS 2782 320A |
| Tensile Stress | 26.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 450 | % | IEC 60811-1-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -30°C | 6.0 | kJ/m² | ISO 180 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Injection instructions |
|---|
| By conventional thermoplastic injection moulding using temperatures set in the range 200°C - 250°C. It is essential to minimise moulding stresses, since these may be released during elevated temperature cure or service, causing warpage. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4200 TFE 10 | RTP Company | PI, TP | RTP |
| WELLAMID Nylon 6000 GS 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Cheng Yu SW15 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| EPIMIX PBT/PET GFR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT+PET | EPIMIX |
| Wuxi Jiahong EB-306 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |