LNP™ THERMOCOMP™ DX11354 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xg3ElY_LNP-THERMOCOMP-DX11354-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This is a PC compound with good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.65 | % | |
| Across Flow : 24 hr | 0.60 to 0.65 | % | |
| Water Absorption (24 hr, 50% RH) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2560 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 59.0 | MPa | |
| Break | 52.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.7 | % | |
| Break | 64 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 91.0 | MPa | |
| Break, 50.0 mm Span | 90.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 124 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (1.00 GHz) | 2.92 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 7.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.600 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 250 to 290 | °C | |
| Middle Temperature | 255 to 295 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 275 to 300 | °C | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SMMA MS 200 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| ENFLEX S3370A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Hifax HSBMCB1158ACLS/2 | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina IVORY PVC COMPOUND -E 105902-35/ 1-Y-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS BT200 | AD majoris | PP, Unspecified | MAJORIS |