Ryton® R-4-222NA
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xfi4wb_Ryton-R-4-222NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® R-4-222NA 40% glass fiber reinforced polyphenylene sulfide compound provides enhanced mechanical strength after constant or repeated exposure to high temperature water and complies with United States Food and Drug Administration (FDA) and European Union (EU 10/2011 and 1183/2012) regulations for use as a component of articles intended for repeat use in contact with all types of foods. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 | % | |
| Across Flow : 3.20 mm | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 103 | ||
| R-Scale | 122 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 186 | MPa | ASTM D638 |
| -- | 190 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 269 | MPa | ASTM D790 |
| -- | 275 | MPa | ISO 178 |
| Compressive Strength | 275 | MPa | ASTM D695 |
| Poisson's Ratio | 0.37 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 91 | J/m | ASTM D256 |
| -- | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 640 | J/m | ASTM D4812 |
| -- | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 1.5E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 8.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.31 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 3.80 | ||
| 25°C, 1 MHz | 3.80 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 2.0E-3 | ||
| 25°C, 1 MHz | 3.0E-3 | ||
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by CP Chemical) | V-0 | UL 94 | |
| Oxygen Index | 45 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Hydrolytic Stability 1 | |||
| Tensile Strength Retained | > 80 | % | |
| Weight Gain | < 1.0 | % |
| Note Message | |
|---|---|
| 1 . | Test specimens aged 1000 hours in water at 140°C (284°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® J (700 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Karina ORANGE PVC COMPOUD 905-32/170-CY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFLAM® RPP 1021 | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |
| EnviroPCABS 2090 HSL | West Michigan Compounding | PC+ABS | EnviroPCABS |
| MARPOL® F-S | Marco Polo International, Inc. | PS (EPS) | MARPOL® |