Aplax P2812GN
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Aplax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xeyeHH_Aplax-P2812GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aplax P2812GN is a 40% mica filled PP product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (1.60 mm) | 0.20 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 59.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 9660 | MPa | ISO 178 |
| Flexural Stress | 97.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | > 165 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, notch 0.25in: 43 kg cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 220 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 170 - 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1600 TFE 20 | RTP Company | PAS | RTP |
| Resinoid 1550 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| SUPREME GPPS SC203EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| ACCUTECH™ ABS831G30L | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| LEXAN™ LAT4000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |