Udel® GF-130

Category:	PSU , Polysulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Udel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	xem9OS_Udel-GF-130.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Udel® GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties and attractive price make these resins particularly effective alternatives to metals in many engineering applications.

Black: Udel® GF-130 BK 937

Natural: Udel® GF-130 NT

General Information
Filler / Reinforcement	Glass Fiber
Features	Acid Resistant Alcohol Resistant Alkali Resistant Good Chemical Resistance Good Creep Resistance Good Dimensional Stability Good Strength High Heat Resistance High Rigidity Hydrocarbon Resistant Hydrolytically Stable
Uses	Appliance Components Appliances Automotive Electronics Electrical Parts Electrical/Electronic Applications Food Service Applications Industrial Parts Microwave Cookware Piping Plumbing Parts Valves/Valve Parts
Agency Ratings	ISO 10993 ISO 10993-Part 1 NSF 61 3
RoHS Compliance	RoHS Compliant
Appearance	Black Natural Color Opaque
Forms	Pellets
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.49	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (343°C/2.16 kg)	6.5	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.20	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8690	MPa	ASTM D638
Tensile Strength	108	MPa	ASTM D638
Tensile Elongation (Break)	2.0	%	ASTM D638
Flexural Modulus	7580	MPa	ASTM D790
Flexural Strength	154	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	69	J/m	ASTM D256
Tensile Impact Strength	113	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	181	°C	ASTM D648

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	2.0E+16	ohms·cm	ASTM D257
Dielectric Strength	19	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
60 Hz	3.48
1 MHz	3.47
Dissipation Factor			ASTM D150
60 Hz	7.0E-4
1 MHz	5.0E-3

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹(3.18 mm)	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature	163 to 191	°C
Drying Time	3.0 to 4.0	hr
Processing (Melt) Temp	343 to 399	°C
Mold Temperature	121 to 163	°C
Injection Rate	Fast
Back Pressure	0.345 to 0.689	MPa
Screw Compression Ratio	2.0:1.0

Note Message
1 .	These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.

Resin Grade	Manufacturer	Category	Trademark
Modified Plastics MAC-FG10 BK	Modified Plastics, Inc.	TP, Unspecified	Modified Plastics
Sylvin 6407-90 Natural	Sylvin Technologies Incorporated	TP, Unspecified	Sylvin
Vibrathane® 6007	Chemtura	PUR-Ester/TDI	Vibrathane®
Braskem PP C123-01N	Braskem Europe GmbH	PP Impact Copolymer	Braskem PP
Fainplast PVC PK 96	Fainplast Compounds S.r.l	PVC, Semi-Rigid	Fainplast PVC