SABIC® LDPE 1965N0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xelqqR_SABIC-LDPE-1965N0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 1965N0 is a fast flowing polymer for flexible articles where mechanical properties are not critical. The material has a typically low tendency to warp. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 65 | g/10 min | |
| 190°C/5.0 kg | 210 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 85.0 | cm³/10min | |
| 190°C/5.0 kg | 270 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 40 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 165 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 8.00 | MPa | |
| Break, 2.00 mm, Compression Molded | 7.00 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 150 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus 1 | ISO 899-1 | ||
| 1 hr | 70.0 | MPa | |
| 1000 hr | 35.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 5.0 | kJ/m² | |
| 23°C, Compression Molded | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 40.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 104 | °C | DIN 53765 |
| Enthalpy Change | 95.0 to 100 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7450 T GK 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| ESTAPROP HK 2540 T8 | Cossa Polimeri S.r.l. | TPO | ESTAPROP |
| FERREX® GPP30CS74UL BLUE | Ferro Corporation | PP Copolymer | FERREX® |
| Grivory® HT1V-4 FWA nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| K-Prene XL-A70 | Technovinyl Polymers India Ltd. | PP+EPDM | K-Prene |