Delrin® 100AL NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xea7t7_Delrin-100AL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lubricated High Viscosity Acetal Homopolymer with Low Wear and Low Friction |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 18 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 170 | kJ/m² | |
| 23°C | 250 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 163 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 8.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R533 NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ALCOM® PA6 900/11 GF10 MR20 SV12-778MCF | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Dryflex® 660800S | ELASTO | SEBS | Dryflex® |
| Formolene® 6144O | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LUVOCOM® 1301/GF/30/TF/15/BK | Lehmann & Voss & Co. | PPS | LUVOCOM® |