Order Products : sales@su-jiao.com
Fainplast CTX 65
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Fainplast Compounds S.r.l |
| Trademark: | Fainplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xcCUvB_Fainplast-CTX-65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This product is a flame retardant silane grafted compound for cable applications, Cross-linkable by heat and moisture by previous addition of a suitable catalyst masterbatch (SIOPLAS method). Application: Sheathing of electrical cables with high flexibility, resistance to harsh weather conditions, oils and hydrocarbons. Standard: EN 50363-2-1 type EM2, EN 50363-2-2 type EM5. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (Natural) | 1.29 | g/cm³ | ISO 1183 |
| Environmental Stress-Cracking Resistance | IEC 60811-4-1 | ||
| Condition A, 50°C, 3.00 mm, 100% Igepal | > 48.0 | hr | |
| Condition B, 50°C, 3.00 mm, 100% Igepal | > 1000 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 60 to 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | > 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 710 | % | ISO 527-2 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811-1-2 | ||
| 100°C, 240 hr | 20 | % | |
| 136°C, 168 hr | -2.0 | % | |
| Change in Ultimate Elongation in Air | IEC 60811-1-2 | ||
| 100°C, 240 hr | -6.0 | % | |
| 136°C, 168 hr | -10 | % | |
| Change in Tensile Strength | IEC 60811-1-2 | ||
| in Sunlight 1 | -10 | % | |
| 100°C, 24 hr, in IRM 902 Oil | -15 | % | |
| 121°C, 18 hr, in IRM 902 Oil | -25 | % | |
| Change in Ultimate Elongation | IEC 60811-1-2 | ||
| in Sunlight 2 | -3.0 | % | |
| 100°C, 24 hr, in IRM 902 Oil | -2.0 | % | |
| 121°C, 18 hr, in IRM 902 Oil | -12 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Flexibility | -62 to -58 | °C | ISO 458 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 155 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 27 to 29 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 135 | °C | |
| Cylinder Zone 3 Temp. | 140 | °C | |
| Cylinder Zone 4 Temp. | 145 | °C | |
| Adapter Temperature | 150 | °C | |
| Die Temperature | 155 | °C |
| Note Message | |
|---|---|
| 1 . | UL 1581 |
| 2 . | UL 1581 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Epoxy E 8701A | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| Multilon® T-2854 | TEIJIN LIMITED | PC+ABS | Multilon® |
| ELASTOSIL® N 2170 | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| Indothene CC | Reliance Industries Limited | LDPE | Indothene |
| ULTEM™ 2110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |