AFFINITY™ PL 1888G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xb9LTO_AFFINITY-PL-1888G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PL 1888G Polyolefin Plastomer for Packaging films is used for high speed packaging applications requiring low seal initiation temperature and good machinability (low consistent coefficient of friction and low block force). This resin is designed to give a COF of < 0.2 for an ~1.0 mil sealant layer in a coextruded film and run fast and trouble-free on most extrusion equipment, including blown film dies equipped with narrow die gaps.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | < 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 5.99 | J | Internal method |
| Film Puncture Force (51 µm) | 67.2 | N | Internal method |
| Film Puncture Resistance (51 µm) | 15.6 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 70.2 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 68.7 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 5.92 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 5.98 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 49.3 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 39.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 600 | % | ASTM D882 |
| TD : Fracture, 51 µm | 570 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 830 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 430 | g | ASTM D1922 |
| TD : 51 µm | 720 | g | ASTM D1922 |
| Seal Initiation Temperature 1(51 µm) | 80.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 98.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 81 | ASTM D2457 | |
| Clarity 2(50.8 µm) | 95.0 | ASTM D1746 | |
| Haze (50.8 µm) | 3.4 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 - 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：改良 LDPE 或中等工作阻隔 模具间隙：70 密尔 (1.8 mm) 熔体温度：430-450°F (221-232°C) 放大比：2.5:1 |
| Note Message | |
|---|---|
| 1 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed on the Instron 10 inches/minute (250 mm/s). |
| 2 . | The ASTM method is under development. BYK-Gardner-Hazeguard Plus has been utilized. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1421J (T38CA) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| APICAL 500AV | Kaneka Corporation | Film, PI | APICAL |
| Durethan® BG 30 X FN01 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| FRblend® PBT-1500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| Kanghui KH2095 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |