BJB Polyurethane ST-1085 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZvqgv_BJB-Polyurethane-ST-1085-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ST-1085 A/B is a tough, multi-purpose polyurethane-polyurea elastomer, useful for many applications and performance requirements. Special product characteristics are as follows:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.06 | g/cm³ | |
| -- 2 | 1.09 | g/cm³ | |
| -- | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.928 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 35.0 | min | |
| Work Time 3(25°C) | 25.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time | 5.0 - 7.0 | day |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.90 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 - 90 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.25 | MPa | ASTM D412 |
| 200% strain | 6.87 | MPa | ASTM D412 |
| 300% strain | 8.40 | MPa | ASTM D412 |
| Tensile Strength (Break) | 14.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength | 44.7 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 55, mixing ratio by capacity: 57 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| 25°C 4 | 1060 | cP | Brookfield |
| 25°C 5 | 6000 | cP | Brookfield |
| 25°C | 3600 | cP | Brookfield |
| Demold Time (25°C) | 240 - 360 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Physical properties obtained from test specimens post cured per recommended procedure.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Part B |
| 5 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 137 | Mitsubishi Chemical Performance Polymers, Inc. | SBS | tefabloc® |
| Nycal™ 2050R33H | Technical Polymers, LLC | Nylon 612 | Nycal™ |
| FLEXAREN® 14006 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| Karina WHITE COLOR CONCENTRATE 10/1-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ RV007ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |