RTP 1201-90A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZYyny_RTP-1201-90A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Glass fiber reinforced polyurethane elastomers offer greater dimensional stability than the base resin. They offer outstanding impact strength and still remain their elastomeric characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 552 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 379 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 16.0 | MPa | ASTM D790 |
| Compressive Strength | 10.3 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| CLTE - Flow | 1.3E-6 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.40 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 6.35mm: 1mm/m. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 210 | °C | |
| Middle Temperature | 188 - 210 | °C | |
| Front Temperature | 182 - 210 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-95A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Capilene® T 77 A | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Dryflex® 400501S | ELASTO | SBS | Dryflex® |
| Latiohm 80-04 PD01 G/30 | LATI S.p.A. | PPS | Latiohm |
| Karina CLEAR PVC COMPOUND 75/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |