RIALFILL H 15 S 40 T0
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xZ34lt_RIALFILL-H-15-S-40-T0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer compound filled with 40% aethetic rigid talc. Flowability specifc for injection molding of aethetic particulars; high rigidity and dimensional planarity at hight temperatures. Available in natural version and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.90 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 28.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 5.0 | % | |
| Flexural Modulus 2(23°C) | 4400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.1 | kJ/m² | |
| 23°C | 2.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 131 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 | |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAPPO™ J100 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Spartech Polycom PP5230F B1-B | Spartech Polycom | PP, Unspecified | Spartech |
| VESTAMID® Care ME62 | Evonik Industries AG | PEBA-Ether | VESTAMID® Care |
| WPP PP UC4X206-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Formolon® 28 | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |