Alathon® L5906
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xXxsFl_Alathon-L5906.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon L5906 is a high molecular weight high density polyethylene homopolymer with a broad bimodal molecular weight distribution. This resin exhibits excellent stiffness, very high tensile strength, and low gels. L5906 is selected by customers for use in draw tapes and paper replacement applications as well as other mono-and multi-layer films requiring both stiffness and toughness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.075 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 20 µm | 1240 | MPa | ASTM D882 |
| TD : 20 µm | 1300 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 40.0 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 35.9 | MPa | ASTM D882 |
| MD : Break, 20 µm | 88.3 | MPa | ASTM D882 |
| TD : Break, 20 µm | 68.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 340 | % | ASTM D882 |
| TD : Break, 20 µm | 340 | % | ASTM D882 |
| Dart Drop Impact 1(20 µm) | 390 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 20 | g | ASTM D1922 |
| TD : 20 µm | 60 | g | ASTM D1922 |
| Extrusion instructions |
|---|
| Film Data Obtained Under the Following Extrusion Conditions:Alpine 200 mm 3 Layer Die (40/35/25); 3 Extruders: 65 mm / 75 mm / 50 mm; Die Gap = 1.5 mm; Film Thickness = 0.8 mil; 500 lbs/ hr; Internal Bubble Cooling; Neck Height = 8 x DD; Blow Up Ratio = 4:1 |
| Note Message | |
|---|---|
| 1 . | f50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PC2510.HF | Guangdong Silver Age Sci & Tech. Co., Ltd | PC+ABS | SILVER® |
| GAPEX® RPP30EA58NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina RED PVC COMPOUND -E711D42/158-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ CR3241 | Sumika Styron Polycarbonate Limited | PC+PET | SD POLYCA™ |
| Sylvin 4200-68 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |