LEXAN™ LAT4000 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xWgsaP_LEXANLAT4000resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP* STAT-LOY* LAT4000 is antistatic compound based on Polycarbonate containing proprietary fillers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.7 | MPa | Internal method |
| Tensile Elongation (Break) | 220 | % | Internal method |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 86.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 830 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 130 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.20 | ASTM D150 | |
| 60 Hz | 3.20 | ASTM D150 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niche PA66BK | Niche Polymer, LLC | Nylon 66 | Niche |
| Ad-Tech Epoxy EA-607 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Geon™ Vinyl Rigid Molding M7500 | PolyOne Corporation | PVC Alloy | Geon™ Vinyl Rigid Molding |
| Laprene® 83FM00A65 | SO.F.TER. SPA | SEBS | Laprene® |
| Sinkral® B 4 Venezia | Versalis S.p.A. | ABS | Sinkral® |