Network Polymers PS HIPS 90 0802
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xWgP6E_Network-Polymers-PS-HIPS-90-0802.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers PS HIPS 90 0802 is a High Impact Polystyrene product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 47 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 1590 | MPa | ASTM D638 |
| Tensile Strength 3(Break) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus 4 | 1930 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 81.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Method I (3 point load), 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP611M | Southern Polymer, Inc. | mLLDPE | PRIMALENE |
| TECHNYL STAR™ SX 216 V60 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Sinkral® C 442 | Versalis S.p.A. | ABS | Sinkral® |
| Fainplast PVC MPH 83 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Kemcor LD 9155 | Qenos Pty Ltd | LDPE | Kemcor |