TECHNYL® A 218 V35 BLACK 21 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xW5tgN_TECHNYL-A-218-V35-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218 V35 Black 21 N is a polyamide 66, reinforced with 35% of glass fibre, heat stabilized, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.41 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.75 | -- | % | |
| Flow | 0.45 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.600 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11400 | 8700 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 210 | 150 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 9800 | -- | MPa | ASTM D790 |
| -- | 9500 | 6800 | MPa | ISO 178 |
| Flexural Stress | 290 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 13 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 2.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ DIDA-E | PolyOne Corporation | Di Isodecyl Adipate | SynPlast™ |
| DIC.PPS Z-200 | DIC Corporation | PPS | DIC.PPS |
| LNP™ LUBRICOMP™ NXCY620 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |
| TOTAL Polypropylene PPR 12236 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Romiloy® 5720/01 | ROMIRA GmbH | PC+PBT | Romiloy® |